For Use at Low-temperature
When employing conveyor chains at low-temperature this kind of as in the fridge or in the cold ambiance, the following problems could occur.
one) Very low temperature brittleness
Generally, a materials is embrittled at low-temperature and shock resistance is lowered. This phenomenon is termed low-temperature brittleness, and the degree of embrittlement differs from material to materials.
The service limit of the conveyor chain depends on its specifications.
2)Influence of freezing
At low-temperature, bending failure, roller rotation failure, repairing of chain, and so on. may very well be triggered through the freezing of penetrated water or deposited frost within the clearance involving pins and bushings, bushings and rollers or inner plates and outer plates. These disorders induce an overload to act around the chain and drive, diminishing the daily life from the chain.
To prevent freezing, generally, it really is suggested to fill 
the clearances using a low-temperature lubricant ideal to the service temperature to prevent water, frost, and so on. from penetrating the respective portions of your chain. For lubrication, a silicon based mostly grease is advised.
For Use at High-temperature
Chains strength is diminished by high-temperature atmosphere, direct conveying of high-temperature loads, or radiated heat, etc. The services restrict at high-temperature depends not within the temperature of the support environment however the temperature and material with the chain entire body.
Following conditions could come about when chains are made use of at high-temperature:
1) High temperature brittleness and fracture by lowered hardness of heat taken care of material
two) Brittleness brought on by carbide precipitation
three) Abnormal put on by scale
4) Fatigue fracture caused by repeated thermal shock (cooling and growth)
5) Abnormal wear as a consequence of an increase inside the coefficient of friction
6) Creep fracture
7) Fracture resulting from thermal fatigue of welded place
8) Effects triggered by thermal growth
?Stiff hyperlinks and rotation failure resulting from decreased clearance ?Fatigue fracture because of lowered fitting force
9）Lubrication failure and stiff backlinks due to deterioration and carbonization of lubricating oil
Grease superb in heat resistance include those dependant on silicon, graphite or molybdenum disulfide.
For use at high-temperature, high-temperature resistance bearings and stainless steel bearings are suggested.